Currently, we have integrated powerful steel plant operating in India at Jamuria. As of December 31, 2020, the aggregate installed metal capacity of our manufacturing plants was 5.71 million tonne per annum (“MTPA”) (comprising intermediate and final products).
Our manufacturing plants also include captive power plants with an aggregate installed capacity of 227 MW, as of December 31, 2020. We are also in the process of increasing the capacities of our existing manufacturing plants and captive power plants, which is expected to increase our aggregate installed metal capacity (comprising of intermediate and final products) from 5.71 MTPA, as of December 31, 2020, to 11.60 MTPA and captive power plants aggregate installed capacity from 227 MW, as of December 31, 2020, to 357 MW.
These proposed expansions are expected to become operational between Fiscal 2022 and Fiscal 2025. In addition, We also have our factories at Mangalpur, Pakuria (installed capacity of 0.04 MTPA) & Giridh in West Bengal.
The following table highlights the installed capacities as of December 31, 2020 and the proposed capacity expansions at our Jamuria manufacturing plant:
Particulars | Existing Installed Capacities as of December 31, 2020* | Proposed Capacity Expansion* |
---|---|---|
Pellet | 1,200,000 TPA | 600,000 TPA |
Sponge iron(1) | 537,900 TPA | 947,100 TPA |
Billet(2) | 491,040 TPA | 653,440 TPA |
Rolling mill and wire rod mill | 350,000 TPA | 744,000 TPA |
Structure mill | 60,000 TPA | – |
Ferro alloy(3) | 70,000 TPA | – |
Blast furnace | – | 600,000 TPA |
Ductile pipe | – | 200,000 TPA |
The assumptions and estimates taken specifically into account include the following:
(1) sponge iron (direct reduced iron): capacity of each kiln in TPD X 330 days per year;
(2) billet: capacity of each furnace in TPH X (24 hours per day/ heat cycle) X 330 days per year; 1 heat cycle = 3 hours;
(3) ferro alloy products: furnace with 1 MVA capacity is equivalent to 1,555.56 TPA. The installed capacity of ferro alloy products may vary depending on the type of ferro alloy produced.